EN 1.4123 Stainless Steel vs. ASTM A387 Grade 21L Class 1

Both EN 1.4123 stainless steel and ASTM A387 grade 21L class 1 are iron alloys. They have 85% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is EN 1.4123 stainless steel and the bottom bar is ASTM A387 grade 21L class 1.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 220 to 250
150
Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
74
Tensile Strength: Ultimate (UTS), MPa 720 to 810
500

Thermal Properties

Latent Heat of Fusion, J/g 280
260
Maximum Temperature: Mechanical, °C 840
480
Melting Completion (Liquidus), °C 1450
1470
Melting Onset (Solidus), °C 1410
1430
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 23
41
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
7.6
Electrical Conductivity: Equal Weight (Specific), % IACS 2.8
8.8

Otherwise Unclassified Properties

Base Metal Price, % relative 10
4.1
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 4.2
1.8
Embodied Energy, MJ/kg 62
23
Embodied Water, L/kg 120
62

Common Calculations

PREN (Pitting Resistance) 24
6.4
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 26 to 29
18
Strength to Weight: Bending, points 23 to 25
18
Thermal Diffusivity, mm2/s 6.3
11
Thermal Shock Resistance, points 26 to 29
14

Alloy Composition

Carbon (C), % 0.35 to 0.5
0 to 0.1
Chromium (Cr), % 14 to 16.5
2.8 to 3.3
Iron (Fe), % 76.7 to 84.6
94.4 to 96.1
Manganese (Mn), % 0 to 1.0
0.3 to 0.6
Molybdenum (Mo), % 1.0 to 2.5
0.9 to 1.1
Nickel (Ni), % 0 to 0.5
0
Nitrogen (N), % 0.1 to 0.3
0
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.025
Vanadium (V), % 0 to 1.5
0