EN 1.4123 Stainless Steel vs. AWS E383

Both EN 1.4123 stainless steel and AWS E383 are iron alloys. They have 52% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.4123 stainless steel and the bottom bar is AWS E383.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
210
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
80
Tensile Strength: Ultimate (UTS), MPa 720 to 810
580

Thermal Properties

Latent Heat of Fusion, J/g 280
320
Melting Completion (Liquidus), °C 1450
1420
Melting Onset (Solidus), °C 1410
1370
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 23
12
Thermal Expansion, µm/m-K 10
14

Otherwise Unclassified Properties

Base Metal Price, % relative 10
37
Density, g/cm3 7.7
8.1
Embodied Carbon, kg CO2/kg material 4.2
6.4
Embodied Energy, MJ/kg 62
89
Embodied Water, L/kg 120
240

Common Calculations

PREN (Pitting Resistance) 24
40
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 26 to 29
20
Strength to Weight: Bending, points 23 to 25
19
Thermal Diffusivity, mm2/s 6.3
3.1
Thermal Shock Resistance, points 26 to 29
15

Alloy Composition

Carbon (C), % 0.35 to 0.5
0 to 0.030
Chromium (Cr), % 14 to 16.5
26.5 to 29
Copper (Cu), % 0
0.6 to 1.5
Iron (Fe), % 76.7 to 84.6
28.8 to 39.2
Manganese (Mn), % 0 to 1.0
0.5 to 2.5
Molybdenum (Mo), % 1.0 to 2.5
3.2 to 4.2
Nickel (Ni), % 0 to 0.5
30 to 33
Nitrogen (N), % 0.1 to 0.3
0
Phosphorus (P), % 0 to 0.040
0 to 0.020
Silicon (Si), % 0 to 1.0
0 to 0.9
Sulfur (S), % 0 to 0.030
0 to 0.020
Vanadium (V), % 0 to 1.5
0