EN 1.4123 Stainless Steel vs. EN 1.3553 Steel

Both EN 1.4123 stainless steel and EN 1.3553 steel are iron alloys. They have 88% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.4123 stainless steel and the bottom bar is EN 1.3553 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 220 to 250
220
Elastic (Young's, Tensile) Modulus, GPa 200
200
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
77
Tensile Strength: Ultimate (UTS), MPa 720 to 810
720

Thermal Properties

Latent Heat of Fusion, J/g 280
260
Maximum Temperature: Mechanical, °C 840
540
Melting Completion (Liquidus), °C 1450
1620
Melting Onset (Solidus), °C 1410
1570
Specific Heat Capacity, J/kg-K 480
440
Thermal Conductivity, W/m-K 23
24
Thermal Expansion, µm/m-K 10
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
10
Electrical Conductivity: Equal Weight (Specific), % IACS 2.8
11

Otherwise Unclassified Properties

Base Metal Price, % relative 10
24
Density, g/cm3 7.7
8.4
Embodied Carbon, kg CO2/kg material 4.2
8.5
Embodied Energy, MJ/kg 62
130
Embodied Water, L/kg 120
96

Common Calculations

PREN (Pitting Resistance) 24
31
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
23
Strength to Weight: Axial, points 26 to 29
24
Strength to Weight: Bending, points 23 to 25
21
Thermal Diffusivity, mm2/s 6.3
6.4
Thermal Shock Resistance, points 26 to 29
21

Alloy Composition

Carbon (C), % 0.35 to 0.5
0.78 to 0.86
Chromium (Cr), % 14 to 16.5
3.9 to 4.3
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 76.7 to 84.6
80.7 to 83.7
Manganese (Mn), % 0 to 1.0
0 to 0.4
Molybdenum (Mo), % 1.0 to 2.5
4.7 to 5.2
Nickel (Ni), % 0 to 0.5
0
Nitrogen (N), % 0.1 to 0.3
0
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 0.4
Sulfur (S), % 0 to 0.030
0 to 0.015
Tungsten (W), % 0
6.0 to 6.7
Vanadium (V), % 0 to 1.5
1.7 to 2.0