EN 1.4123 Stainless Steel vs. EN 1.4529 Stainless Steel

Both EN 1.4123 stainless steel and EN 1.4529 stainless steel are iron alloys. They have 65% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is EN 1.4123 stainless steel and the bottom bar is EN 1.4529 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 220 to 250
220
Elastic (Young's, Tensile) Modulus, GPa 200
200
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
80
Tensile Strength: Ultimate (UTS), MPa 720 to 810
750

Thermal Properties

Latent Heat of Fusion, J/g 280
300
Maximum Temperature: Corrosion, °C 390
420
Maximum Temperature: Mechanical, °C 840
1100
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1410
1410
Specific Heat Capacity, J/kg-K 480
460
Thermal Conductivity, W/m-K 23
12
Thermal Expansion, µm/m-K 10
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.8
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 10
33
Density, g/cm3 7.7
8.1
Embodied Carbon, kg CO2/kg material 4.2
6.2
Embodied Energy, MJ/kg 62
84
Embodied Water, L/kg 120
200

Common Calculations

PREN (Pitting Resistance) 24
45
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 26 to 29
26
Strength to Weight: Bending, points 23 to 25
23
Thermal Diffusivity, mm2/s 6.3
3.2
Thermal Shock Resistance, points 26 to 29
17

Alloy Composition

Carbon (C), % 0.35 to 0.5
0 to 0.020
Chromium (Cr), % 14 to 16.5
19 to 21
Copper (Cu), % 0
0.5 to 1.5
Iron (Fe), % 76.7 to 84.6
42.7 to 50.4
Manganese (Mn), % 0 to 1.0
0 to 1.0
Molybdenum (Mo), % 1.0 to 2.5
6.0 to 7.0
Nickel (Ni), % 0 to 0.5
24 to 26
Nitrogen (N), % 0.1 to 0.3
0.15 to 0.25
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0 to 1.0
0 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.010
Vanadium (V), % 0 to 1.5
0