EN 1.4123 Stainless Steel vs. EN 1.4571 Stainless Steel

Both EN 1.4123 stainless steel and EN 1.4571 stainless steel are iron alloys. They have 85% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.4123 stainless steel and the bottom bar is EN 1.4571 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 220 to 250
190 to 270
Elastic (Young's, Tensile) Modulus, GPa 200
200
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
78
Tensile Strength: Ultimate (UTS), MPa 720 to 810
600 to 900

Thermal Properties

Latent Heat of Fusion, J/g 280
290
Maximum Temperature: Corrosion, °C 390
480
Maximum Temperature: Mechanical, °C 840
950
Melting Completion (Liquidus), °C 1450
1440
Melting Onset (Solidus), °C 1410
1400
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 23
15
Thermal Expansion, µm/m-K 10
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.8
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 10
19
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 4.2
3.9
Embodied Energy, MJ/kg 62
54
Embodied Water, L/kg 120
150

Common Calculations

PREN (Pitting Resistance) 24
25
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 26 to 29
21 to 32
Strength to Weight: Bending, points 23 to 25
20 to 26
Thermal Diffusivity, mm2/s 6.3
4.0
Thermal Shock Resistance, points 26 to 29
13 to 20

Alloy Composition

Carbon (C), % 0.35 to 0.5
0 to 0.080
Chromium (Cr), % 14 to 16.5
16.5 to 18.5
Iron (Fe), % 76.7 to 84.6
61.7 to 71
Manganese (Mn), % 0 to 1.0
0 to 2.0
Molybdenum (Mo), % 1.0 to 2.5
2.0 to 2.5
Nickel (Ni), % 0 to 0.5
10.5 to 13.5
Nitrogen (N), % 0.1 to 0.3
0
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.015
Titanium (Ti), % 0
0 to 0.7
Vanadium (V), % 0 to 1.5
0