EN 1.4325 Stainless Steel vs. SAE-AISI 4012 Steel

Both EN 1.4325 stainless steel and SAE-AISI 4012 steel are iron alloys. They have 73% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4325 stainless steel and the bottom bar is SAE-AISI 4012 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
130
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 45
23
Fatigue Strength, MPa 190
160
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Shear Strength, MPa 450
270
Tensile Strength: Ultimate (UTS), MPa 650
420
Tensile Strength: Yield (Proof), MPa 210
220

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 930
400
Melting Completion (Liquidus), °C 1430
1460
Melting Onset (Solidus), °C 1380
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 16
51
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.8
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 15
2.1
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.0
1.5
Embodied Energy, MJ/kg 42
19
Embodied Water, L/kg 140
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 230
82
Resilience: Unit (Modulus of Resilience), kJ/m3 110
130
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 23
15
Strength to Weight: Bending, points 21
16
Thermal Diffusivity, mm2/s 4.3
14
Thermal Shock Resistance, points 15
12

Alloy Composition

Carbon (C), % 0.030 to 0.15
0.090 to 0.14
Chromium (Cr), % 17 to 19
0
Iron (Fe), % 67.8 to 75
98.2 to 98.9
Manganese (Mn), % 0 to 2.0
0.75 to 1.0
Molybdenum (Mo), % 0
0.15 to 0.25
Nickel (Ni), % 8.0 to 10
0
Phosphorus (P), % 0 to 0.045
0 to 0.035
Silicon (Si), % 0 to 1.0
0.15 to 0.35
Sulfur (S), % 0 to 0.030
0 to 0.040