EN 1.4374 Stainless Steel vs. C77100 Nickel Silver
EN 1.4374 stainless steel belongs to the iron alloys classification, while C77100 nickel silver belongs to the copper alloys. There are 26 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is EN 1.4374 stainless steel and the bottom bar is C77100 nickel silver.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 110 |
| Poisson's Ratio | 0.28 | |
| 0.31 |
| Shear Modulus, GPa | 77 | |
| 45 |
| Tensile Strength: Ultimate (UTS), MPa | 800 | |
| 600 |
| Tensile Strength: Yield (Proof), MPa | 400 | |
| 540 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 180 |
| Maximum Temperature: Mechanical, °C | 920 | |
| 150 |
| Melting Completion (Liquidus), °C | 1400 | |
| 990 |
| Melting Onset (Solidus), °C | 1360 | |
| 950 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 390 |
| Thermal Conductivity, W/m-K | 15 | |
| 40 |
| Thermal Expansion, µm/m-K | 17 | |
| 20 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.4 | |
| 7.6 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.9 | |
| 8.5 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 14 | |
| 27 |
| Density, g/cm3 | 7.7 | |
| 8.1 |
| Embodied Carbon, kg CO2/kg material | 2.9 | |
| 3.5 |
| Embodied Energy, MJ/kg | 42 | |
| 56 |
| Embodied Water, L/kg | 150 | |
| 310 |
Common Calculations
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 400 | |
| 1280 |
| Stiffness to Weight: Axial, points | 14 | |
| 7.8 |
| Stiffness to Weight: Bending, points | 25 | |
| 20 |
| Strength to Weight: Axial, points | 29 | |
| 21 |
| Strength to Weight: Bending, points | 25 | |
| 20 |
| Thermal Diffusivity, mm2/s | 4.0 | |
| 13 |
| Thermal Shock Resistance, points | 17 | |
| 19 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Carbon (C), % | 0.050 to 0.1 | |
| 0 |
| Chromium (Cr), % | 17.5 to 18.5 | |
| 0 |
| Copper (Cu), % | 0 to 0.4 | |
| 52 to 56 |
| Iron (Fe), % | 63.5 to 67.9 | |
| 0 |
| Lead (Pb), % | 0 | |
| 0 to 0.030 |
| Manganese (Mn), % | 9.0 to 10 | |
| 0 to 0.9 |
| Molybdenum (Mo), % | 0 to 0.5 | |
| 0 |
| Nickel (Ni), % | 5.0 to 6.0 | |
| 9.0 to 12 |
| Nitrogen (N), % | 0.25 to 0.32 | |
| 0 |
| Phosphorus (P), % | 0 to 0.035 | |
| 0 |
| Silicon (Si), % | 0.3 to 0.6 | |
| 0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 30.6 to 39 |
| Residuals, % | 0 | |
| 0 to 0.5 |