EN 1.4410 Stainless Steel vs. EN 1.4024 Stainless Steel

Both EN 1.4410 stainless steel and EN 1.4024 stainless steel are iron alloys. They have 76% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4410 stainless steel and the bottom bar is EN 1.4024 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 24
15 to 22
Fatigue Strength, MPa 410
220 to 300
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 81
76
Shear Strength, MPa 540
370 to 460
Tensile Strength: Ultimate (UTS), MPa 850
590 to 750
Tensile Strength: Yield (Proof), MPa 600
330 to 510

Thermal Properties

Latent Heat of Fusion, J/g 300
270
Maximum Temperature: Corrosion, °C 450
390
Maximum Temperature: Mechanical, °C 1100
760
Melting Completion (Liquidus), °C 1450
1440
Melting Onset (Solidus), °C 1400
1400
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 15
30
Thermal Expansion, µm/m-K 13
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 20
7.0
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 4.0
1.9
Embodied Energy, MJ/kg 56
27
Embodied Water, L/kg 180
100

Common Calculations

PREN (Pitting Resistance) 42
13
Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
98 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 880
280 to 660
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 30
21 to 27
Strength to Weight: Bending, points 26
20 to 24
Thermal Diffusivity, mm2/s 4.0
8.1
Thermal Shock Resistance, points 23
21 to 26

Alloy Composition

Carbon (C), % 0 to 0.030
0.12 to 0.17
Chromium (Cr), % 24 to 26
12 to 14
Iron (Fe), % 58.1 to 66.8
83.8 to 87.9
Manganese (Mn), % 0 to 2.0
0 to 1.0
Molybdenum (Mo), % 3.0 to 4.5
0
Nickel (Ni), % 6.0 to 8.0
0
Nitrogen (N), % 0.24 to 0.35
0
Phosphorus (P), % 0 to 0.035
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.015
0 to 0.015