EN 1.4024 (X15Cr13) Stainless Steel
EN 1.4024 stainless steel is a martensitic stainless steel formulated for primary forming into wrought products. 1.4024 is the EN numeric designation for this material. X15Cr13 is the EN chemical designation.
It has a moderately low embodied energy among the wrought martensitic stainless steels in the database.
The properties of EN 1.4024 stainless steel include three common variations. This page shows summary ranges across all of them. For more specific values, follow the links immediately below. The graph bars on the material properties cards further below compare EN 1.4024 stainless steel to: wrought martensitic stainless steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Elastic (Young's, Tensile) Modulus
190 GPa 28 x 106 psi
Elongation at Break
15 to 22 %
Fatigue Strength
220 to 300 MPa 32 to 43 x 103 psi
Poisson's Ratio
0.28
Shear Modulus
76 GPa 11 x 106 psi
Shear Strength
370 to 460 MPa 54 to 66 x 103 psi
Tensile Strength: Ultimate (UTS)
590 to 750 MPa 85 to 110 x 103 psi
Tensile Strength: Yield (Proof)
330 to 510 MPa 48 to 74 x 103 psi
Thermal Properties
Latent Heat of Fusion
270 J/g
Maximum Temperature: Corrosion
390 °C 730 °F
Maximum Temperature: Mechanical
760 °C 1390 °F
Melting Completion (Liquidus)
1440 °C 2630 °F
Melting Onset (Solidus)
1400 °C 2550 °F
Specific Heat Capacity
480 J/kg-K 0.11 BTU/lb-°F
Thermal Conductivity
30 W/m-K 17 BTU/h-ft-°F
Thermal Expansion
11 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
2.9 % IACS
Electrical Conductivity: Equal Weight (Specific)
3.3 % IACS
Otherwise Unclassified Properties
Base Metal Price
7.0 % relative
Density
7.7 g/cm3 480 lb/ft3
Embodied Carbon
1.9 kg CO2/kg material
Embodied Energy
27 MJ/kg 12 x 103 BTU/lb
Embodied Water
100 L/kg 12 gal/lb
Common Calculations
PREN (Pitting Resistance)
13
Resilience: Ultimate (Unit Rupture Work)
98 to 110 MJ/m3
Resilience: Unit (Modulus of Resilience)
280 to 660 kJ/m3
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
25 points
Strength to Weight: Axial
21 to 27 points
Strength to Weight: Bending
20 to 24 points
Thermal Diffusivity
8.1 mm2/s
Thermal Shock Resistance
21 to 26 points
Alloy Composition
Among wrought stainless steels, the composition of EN 1.4024 stainless steel is notable for containing comparatively high amounts of chromium (Cr) and manganese (Mn). Chromium is the defining alloying element of stainless steel. Higher chromium content imparts additional corrosion resistance. Manganese is used to improve ductility at elevated temperatures. It also permits a higher nitrogen content than would otherwise be possible.
| Fe | 83.8 to 87.9 | |
| Cr | 12 to 14 | |
| Mn | 0 to 1.0 | |
| Si | 0 to 1.0 | |
| C | 0.12 to 0.17 | |
| P | 0 to 0.040 | |
| S | 0 to 0.015 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Similar Alloys
Further Reading
EN 10088-2: Stainless steels - Part 2: Technical delivery conditions for sheet/plate and strip of corrosion resisting steels for general purposes
EN 10088-3: Stainless steels - Part 3: Technical delivery conditions for semi-finished products, bars, rods, wire, sections and bright products of corrosion resisting steels for general purposes
EN 10088-1: Stainless steels - Part 1: List of stainless steels
Corrosion of Stainless Steels, A. John Sedriks, 1996
Advances in Stainless Steels, Baldev Raj et al. (editors), 2010
CRC Materials Science and Engineering Handbook, 4th ed., James F. Shackelford et al. (editors), 2015