EN 1.4410 Stainless Steel vs. EN 1.4931 Steel

Both EN 1.4410 stainless steel and EN 1.4931 steel are iron alloys. They have 77% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4410 stainless steel and the bottom bar is EN 1.4931 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 260
240
Elastic (Young's, Tensile) Modulus, GPa 210
200
Elongation at Break, % 24
17
Fatigue Strength, MPa 410
410
Impact Strength: V-Notched Charpy, J 90
30
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 81
76
Tensile Strength: Ultimate (UTS), MPa 850
810
Tensile Strength: Yield (Proof), MPa 600
620

Thermal Properties

Latent Heat of Fusion, J/g 300
270
Maximum Temperature: Mechanical, °C 1100
600
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
24
Thermal Expansion, µm/m-K 13
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
9.8
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
11

Otherwise Unclassified Properties

Base Metal Price, % relative 20
8.5
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 4.0
2.9
Embodied Energy, MJ/kg 56
42
Embodied Water, L/kg 180
100

Common Calculations

PREN (Pitting Resistance) 42
16
Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
130
Resilience: Unit (Modulus of Resilience), kJ/m3 880
970
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 30
29
Strength to Weight: Bending, points 26
25
Thermal Diffusivity, mm2/s 4.0
6.5
Thermal Shock Resistance, points 23
22

Alloy Composition

Carbon (C), % 0 to 0.030
0.2 to 0.26
Chromium (Cr), % 24 to 26
11.3 to 12.2
Iron (Fe), % 58.1 to 66.8
83.2 to 86.8
Manganese (Mn), % 0 to 2.0
0.5 to 0.8
Molybdenum (Mo), % 3.0 to 4.5
1.0 to 1.2
Nickel (Ni), % 6.0 to 8.0
0 to 1.0
Nitrogen (N), % 0.24 to 0.35
0
Phosphorus (P), % 0 to 0.035
0 to 0.030
Silicon (Si), % 0 to 1.0
0 to 0.4
Sulfur (S), % 0 to 0.015
0 to 0.020
Tungsten (W), % 0
0 to 0.5
Vanadium (V), % 0
0.25 to 0.35