EN 1.4419 Stainless Steel vs. SAE-AISI 4621 Steel

Both EN 1.4419 stainless steel and SAE-AISI 4621 steel are iron alloys. They have 85% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4419 stainless steel and the bottom bar is SAE-AISI 4621 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 11 to 17
27
Fatigue Strength, MPa 230 to 680
270
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Shear Strength, MPa 410 to 950
320
Tensile Strength: Ultimate (UTS), MPa 660 to 1590
500
Tensile Strength: Yield (Proof), MPa 370 to 1240
360

Thermal Properties

Latent Heat of Fusion, J/g 280
250
Maximum Temperature: Mechanical, °C 790
410
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 30
46
Thermal Expansion, µm/m-K 11
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.8
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 3.2
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 8.0
3.3
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 2.2
1.6
Embodied Energy, MJ/kg 30
22
Embodied Water, L/kg 110
50

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 95 to 170
120
Resilience: Unit (Modulus of Resilience), kJ/m3 350 to 3920
340
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 24 to 57
18
Strength to Weight: Bending, points 22 to 39
18
Thermal Diffusivity, mm2/s 8.1
12
Thermal Shock Resistance, points 23 to 55
15

Alloy Composition

Carbon (C), % 0.36 to 0.42
0.18 to 0.23
Chromium (Cr), % 13 to 14.5
0
Iron (Fe), % 82 to 86
96.1 to 97.1
Manganese (Mn), % 0 to 1.0
0.7 to 0.9
Molybdenum (Mo), % 0.6 to 1.0
0.2 to 0.3
Nickel (Ni), % 0
1.7 to 2.0
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0 to 1.0
0.15 to 0.35
Sulfur (S), % 0 to 0.015
0 to 0.040