EN 1.4451 Stainless Steel vs. EN 1.4011 Stainless Steel

Both EN 1.4451 stainless steel and EN 1.4011 stainless steel are iron alloys. They have 75% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4451 stainless steel and the bottom bar is EN 1.4011 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 25
17
Fatigue Strength, MPa 370
310
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 80
76
Tensile Strength: Ultimate (UTS), MPa 750
700
Tensile Strength: Yield (Proof), MPa 540
510

Thermal Properties

Latent Heat of Fusion, J/g 300
270
Maximum Temperature: Corrosion, °C 450
390
Maximum Temperature: Mechanical, °C 1100
750
Melting Completion (Liquidus), °C 1430
1450
Melting Onset (Solidus), °C 1380
1400
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 17
25
Thermal Expansion, µm/m-K 17
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
3.4

Otherwise Unclassified Properties

Base Metal Price, % relative 20
7.0
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.8
2.0
Embodied Energy, MJ/kg 53
28
Embodied Water, L/kg 190
100

Common Calculations

PREN (Pitting Resistance) 39
13
Resilience: Ultimate (Unit Rupture Work), MJ/m3 170
110
Resilience: Unit (Modulus of Resilience), kJ/m3 710
660
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 27
25
Strength to Weight: Bending, points 23
23
Thermal Diffusivity, mm2/s 4.5
6.7
Thermal Shock Resistance, points 16
24

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.15
Chromium (Cr), % 25 to 27
11.5 to 13.5
Copper (Cu), % 2.8 to 3.5
0
Iron (Fe), % 56.2 to 64.6
82.8 to 88.5
Manganese (Mn), % 0 to 1.5
0 to 1.0
Molybdenum (Mo), % 2.5 to 3.5
0 to 0.5
Nickel (Ni), % 5.0 to 7.0
0 to 1.0
Nitrogen (N), % 0.12 to 0.22
0
Phosphorus (P), % 0 to 0.035
0 to 0.035
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.025