MakeItFrom.com
Menu (ESC)

EN 1.4458 Stainless Steel vs. EN 1.0070 Steel

Both EN 1.4458 stainless steel and EN 1.0070 steel are iron alloys. They have 47% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.4458 stainless steel and the bottom bar is EN 1.0070 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
210
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 34
9.1
Fatigue Strength, MPa 150
210
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
73
Tensile Strength: Ultimate (UTS), MPa 510
740
Tensile Strength: Yield (Proof), MPa 190
350

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1420
1470
Melting Onset (Solidus), °C 1370
1430
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 16
53
Thermal Expansion, µm/m-K 15
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
6.8
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
7.8

Otherwise Unclassified Properties

Base Metal Price, % relative 30
1.7
Density, g/cm3 8.0
7.9
Embodied Carbon, kg CO2/kg material 5.4
1.4
Embodied Energy, MJ/kg 75
18
Embodied Water, L/kg 200
45

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
56
Resilience: Unit (Modulus of Resilience), kJ/m3 89
320
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 17
26
Strength to Weight: Bending, points 18
23
Thermal Diffusivity, mm2/s 4.2
14
Thermal Shock Resistance, points 12
23

Alloy Composition

Carbon (C), % 0 to 0.030
0
Chromium (Cr), % 19 to 22
0
Copper (Cu), % 0 to 2.0
0
Iron (Fe), % 40.2 to 53
99.876 to 100
Manganese (Mn), % 0 to 2.0
0
Molybdenum (Mo), % 2.0 to 2.5
0
Nickel (Ni), % 26 to 30
0
Nitrogen (N), % 0 to 0.2
0 to 0.014
Phosphorus (P), % 0 to 0.035
0 to 0.055
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.025
0 to 0.055