EN 1.4490 Stainless Steel vs. ASTM A210 Steel

Both EN 1.4490 stainless steel and ASTM A210 steel are iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.4490 stainless steel and the bottom bar is ASTM A210 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 34
34
Fatigue Strength, MPa 210
230 to 250
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
73
Tensile Strength: Ultimate (UTS), MPa 560
470 to 540
Tensile Strength: Yield (Proof), MPa 260
290 to 310

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 990
400
Melting Completion (Liquidus), °C 1440
1460 to 1470
Melting Onset (Solidus), °C 1390
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
52 to 53
Thermal Expansion, µm/m-K 12
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.0 to 8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 19
1.8
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 3.7
1.4
Embodied Energy, MJ/kg 52
18
Embodied Water, L/kg 150
45 to 46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 160
140 to 160
Resilience: Unit (Modulus of Resilience), kJ/m3 170
230 to 250
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 20
17 to 19
Strength to Weight: Bending, points 19
17 to 19
Thermal Diffusivity, mm2/s 4.1
14
Thermal Shock Resistance, points 16
15 to 17