EN 1.4509 Stainless Steel vs. AISI 310H Stainless Steel

Both EN 1.4509 stainless steel and AISI 310H stainless steel are iron alloys. Both are furnished in the annealed condition. They have 72% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4509 stainless steel and the bottom bar is AISI 310H stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
190
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 21
40
Fatigue Strength, MPa 170
200
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 77
79
Shear Strength, MPa 330
400
Tensile Strength: Ultimate (UTS), MPa 530
580
Tensile Strength: Yield (Proof), MPa 260
230

Thermal Properties

Latent Heat of Fusion, J/g 280
300
Maximum Temperature: Corrosion, °C 570
450
Maximum Temperature: Mechanical, °C 890
1100
Melting Completion (Liquidus), °C 1440
1410
Melting Onset (Solidus), °C 1400
1360
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 25
15
Thermal Expansion, µm/m-K 10
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 3.4
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 13
25
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 2.8
4.3
Embodied Energy, MJ/kg 41
61
Embodied Water, L/kg 120
190

Common Calculations

PREN (Pitting Resistance) 18
25
Resilience: Ultimate (Unit Rupture Work), MJ/m3 90
190
Resilience: Unit (Modulus of Resilience), kJ/m3 180
130
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 19
21
Strength to Weight: Bending, points 19
20
Thermal Diffusivity, mm2/s 6.8
3.9
Thermal Shock Resistance, points 19
13

Alloy Composition

Carbon (C), % 0 to 0.030
0.040 to 0.1
Chromium (Cr), % 17.5 to 18.5
24 to 26
Iron (Fe), % 77.8 to 82.1
49.1 to 57
Manganese (Mn), % 0 to 1.0
0 to 2.0
Nickel (Ni), % 0
19 to 22
Niobium (Nb), % 0.3 to 1.0
0
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 0 to 1.0
0 to 0.75
Sulfur (S), % 0 to 0.015
0 to 0.030
Titanium (Ti), % 0.1 to 0.6
0