EN 1.4518 Stainless Steel vs. AISI 304N Stainless Steel

Both EN 1.4518 stainless steel and AISI 304N stainless steel are iron alloys. They have a very high 95% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4518 stainless steel and the bottom bar is AISI 304N stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34
9.1 to 45
Fatigue Strength, MPa 160
220 to 440
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 79
77
Tensile Strength: Ultimate (UTS), MPa 490
620 to 1180
Tensile Strength: Yield (Proof), MPa 210
270 to 850

Thermal Properties

Latent Heat of Fusion, J/g 300
290
Maximum Temperature: Corrosion, °C 420
420
Maximum Temperature: Mechanical, °C 1000
960
Melting Completion (Liquidus), °C 1450
1420
Melting Onset (Solidus), °C 1400
1380
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 15
16
Thermal Expansion, µm/m-K 12
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.7

Otherwise Unclassified Properties

Base Metal Price, % relative 20
15
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 4.0
3.0
Embodied Energy, MJ/kg 55
43
Embodied Water, L/kg 160
150

Common Calculations

PREN (Pitting Resistance) 30
21
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
98 to 280
Resilience: Unit (Modulus of Resilience), kJ/m3 100
180 to 1830
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 17
22 to 42
Strength to Weight: Bending, points 18
21 to 32
Thermal Diffusivity, mm2/s 4.1
4.2
Thermal Shock Resistance, points 14
14 to 26

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.080
Chromium (Cr), % 18 to 20
18 to 20
Iron (Fe), % 61.4 to 70
66.4 to 73.9
Manganese (Mn), % 0 to 1.5
0 to 2.0
Molybdenum (Mo), % 3.0 to 3.5
0
Nickel (Ni), % 9.0 to 12
8.0 to 10.5
Nitrogen (N), % 0
0.1 to 0.16
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 0 to 1.5
0 to 0.75
Sulfur (S), % 0 to 0.030
0 to 0.030