EN 1.4518 Stainless Steel vs. AISI 445 Stainless Steel

Both EN 1.4518 stainless steel and AISI 445 stainless steel are iron alloys. They have 86% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.4518 stainless steel and the bottom bar is AISI 445 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34
25
Fatigue Strength, MPa 160
160
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 79
78
Tensile Strength: Ultimate (UTS), MPa 490
480
Tensile Strength: Yield (Proof), MPa 210
230

Thermal Properties

Latent Heat of Fusion, J/g 300
290
Maximum Temperature: Corrosion, °C 420
480
Maximum Temperature: Mechanical, °C 1000
950
Melting Completion (Liquidus), °C 1450
1440
Melting Onset (Solidus), °C 1400
1390
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 15
21
Thermal Expansion, µm/m-K 12
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
2.6
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
3.0

Otherwise Unclassified Properties

Base Metal Price, % relative 20
12
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 4.0
2.6
Embodied Energy, MJ/kg 55
38
Embodied Water, L/kg 160
130

Common Calculations

PREN (Pitting Resistance) 30
20
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
98
Resilience: Unit (Modulus of Resilience), kJ/m3 100
140
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 17
17
Strength to Weight: Bending, points 18
18
Thermal Diffusivity, mm2/s 4.1
5.6
Thermal Shock Resistance, points 14
16

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.020
Chromium (Cr), % 18 to 20
19 to 21
Copper (Cu), % 0
0.3 to 0.6
Iron (Fe), % 61.4 to 70
74.9 to 80.7
Manganese (Mn), % 0 to 1.5
0 to 1.0
Molybdenum (Mo), % 3.0 to 3.5
0
Nickel (Ni), % 9.0 to 12
0 to 0.6
Niobium (Nb), % 0
0 to 0.8
Nitrogen (N), % 0
0 to 0.030
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.5
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.012