EN 1.4518 Stainless Steel vs. ASTM A209 Steel

Both EN 1.4518 stainless steel and ASTM A209 steel are iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.4518 stainless steel and the bottom bar is ASTM A209 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 34
34
Fatigue Strength, MPa 160
180 to 200
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 79
73
Tensile Strength: Ultimate (UTS), MPa 490
420 to 460
Tensile Strength: Yield (Proof), MPa 210
220 to 250

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1000
410
Melting Completion (Liquidus), °C 1450
1470
Melting Onset (Solidus), °C 1400
1420 to 1430
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 15
50
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
8.1 to 8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 20
2.4
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 4.0
1.5
Embodied Energy, MJ/kg 55
20
Embodied Water, L/kg 160
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
120 to 130
Resilience: Unit (Modulus of Resilience), kJ/m3 100
130 to 170
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 17
15 to 16
Strength to Weight: Bending, points 18
16 to 17
Thermal Diffusivity, mm2/s 4.1
13
Thermal Shock Resistance, points 14
12 to 14