EN 1.4518 Stainless Steel vs. AWS BAg-7

EN 1.4518 stainless steel belongs to the iron alloys classification, while AWS BAg-7 belongs to the otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.

For each property being compared, the top bar is EN 1.4518 stainless steel and the bottom bar is AWS BAg-7.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
83
Poisson's Ratio 0.28
0.34
Shear Modulus, GPa 79
31
Tensile Strength: Ultimate (UTS), MPa 490
150

Thermal Properties

Latent Heat of Fusion, J/g 300
130
Melting Completion (Liquidus), °C 1450
650
Melting Onset (Solidus), °C 1400
620
Specific Heat Capacity, J/kg-K 470
290
Thermal Expansion, µm/m-K 12
20

Otherwise Unclassified Properties

Density, g/cm3 7.9
9.3
Embodied Carbon, kg CO2/kg material 4.0
55
Embodied Energy, MJ/kg 55
860

Common Calculations

Stiffness to Weight: Axial, points 14
4.9
Stiffness to Weight: Bending, points 25
16
Strength to Weight: Axial, points 17
4.5
Strength to Weight: Bending, points 18
6.7
Thermal Shock Resistance, points 14
6.4

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Carbon (C), % 0 to 0.030
0
Chromium (Cr), % 18 to 20
0
Copper (Cu), % 0
21 to 23
Iron (Fe), % 61.4 to 70
0
Manganese (Mn), % 0 to 1.5
0
Molybdenum (Mo), % 3.0 to 3.5
0
Nickel (Ni), % 9.0 to 12
0
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0 to 1.5
0
Silver (Ag), % 0
55 to 57
Sulfur (S), % 0 to 0.030
0
Tin (Sn), % 0
4.5 to 5.5
Zinc (Zn), % 0
15 to 19
Residuals, % 0
0 to 0.15