EN 1.4518 Stainless Steel vs. EN 1.4361 Stainless Steel

Both EN 1.4518 stainless steel and EN 1.4361 stainless steel are iron alloys. Both are furnished in the solution annealed (AT) condition. They have a moderately high 92% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4518 stainless steel and the bottom bar is EN 1.4361 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 34
43
Fatigue Strength, MPa 160
220
Impact Strength: V-Notched Charpy, J 90
90
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 79
75
Tensile Strength: Ultimate (UTS), MPa 490
630
Tensile Strength: Yield (Proof), MPa 210
250

Thermal Properties

Latent Heat of Fusion, J/g 300
350
Maximum Temperature: Corrosion, °C 420
410
Maximum Temperature: Mechanical, °C 1000
940
Melting Completion (Liquidus), °C 1450
1370
Melting Onset (Solidus), °C 1400
1330
Specific Heat Capacity, J/kg-K 470
490
Thermal Conductivity, W/m-K 15
14
Thermal Expansion, µm/m-K 12
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 20
19
Density, g/cm3 7.9
7.6
Embodied Carbon, kg CO2/kg material 4.0
3.6
Embodied Energy, MJ/kg 55
52
Embodied Water, L/kg 160
150

Common Calculations

PREN (Pitting Resistance) 30
19
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
220
Resilience: Unit (Modulus of Resilience), kJ/m3 100
160
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 17
23
Strength to Weight: Bending, points 18
21
Thermal Diffusivity, mm2/s 4.1
3.7
Thermal Shock Resistance, points 14
15

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.015
Chromium (Cr), % 18 to 20
16.5 to 18.5
Iron (Fe), % 61.4 to 70
58.7 to 65.8
Manganese (Mn), % 0 to 1.5
0 to 2.0
Molybdenum (Mo), % 3.0 to 3.5
0 to 0.2
Nickel (Ni), % 9.0 to 12
14 to 16
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 1.5
3.7 to 4.5
Sulfur (S), % 0 to 0.030
0 to 0.010