EN 1.4518 Stainless Steel vs. EN 1.4807 Stainless Steel

Both EN 1.4518 stainless steel and EN 1.4807 stainless steel are iron alloys. They have 72% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4518 stainless steel and the bottom bar is EN 1.4807 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 34
4.5
Fatigue Strength, MPa 160
120
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 79
75
Tensile Strength: Ultimate (UTS), MPa 490
480
Tensile Strength: Yield (Proof), MPa 210
250

Thermal Properties

Latent Heat of Fusion, J/g 300
320
Maximum Temperature: Corrosion, °C 420
600
Maximum Temperature: Mechanical, °C 1000
1000
Melting Completion (Liquidus), °C 1450
1390
Melting Onset (Solidus), °C 1400
1350
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 15
12
Thermal Expansion, µm/m-K 12
15

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 20
39
Density, g/cm3 7.9
8.0
Embodied Carbon, kg CO2/kg material 4.0
6.8
Embodied Energy, MJ/kg 55
97
Embodied Water, L/kg 160
190

Common Calculations

PREN (Pitting Resistance) 30
19
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
18
Resilience: Unit (Modulus of Resilience), kJ/m3 100
160
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 17
17
Strength to Weight: Bending, points 18
17
Thermal Diffusivity, mm2/s 4.1
3.2
Thermal Shock Resistance, points 14
12

Alloy Composition

Carbon (C), % 0 to 0.030
0.3 to 0.5
Chromium (Cr), % 18 to 20
17 to 20
Iron (Fe), % 61.4 to 70
36.6 to 46.7
Manganese (Mn), % 0 to 1.5
0 to 2.0
Molybdenum (Mo), % 3.0 to 3.5
0 to 0.5
Nickel (Ni), % 9.0 to 12
34 to 36
Niobium (Nb), % 0
1.0 to 1.8
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.5
1.0 to 2.5
Sulfur (S), % 0 to 0.030
0 to 0.030