EN 1.4518 Stainless Steel vs. EN 1.7176 Steel

Both EN 1.4518 stainless steel and EN 1.7176 steel are iron alloys. They have 68% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is EN 1.4518 stainless steel and the bottom bar is EN 1.7176 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 79
73
Tensile Strength: Ultimate (UTS), MPa 490
670 to 2010

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1000
420
Melting Completion (Liquidus), °C 1450
1450
Melting Onset (Solidus), °C 1400
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 15
48
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 20
2.1
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 4.0
1.4
Embodied Energy, MJ/kg 55
19
Embodied Water, L/kg 160
50

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 17
24 to 71
Strength to Weight: Bending, points 18
22 to 45
Thermal Diffusivity, mm2/s 4.1
13
Thermal Shock Resistance, points 14
20 to 59

Alloy Composition

Carbon (C), % 0 to 0.030
0.52 to 0.59
Chromium (Cr), % 18 to 20
0.7 to 1.0
Iron (Fe), % 61.4 to 70
97 to 98.1
Manganese (Mn), % 0 to 1.5
0.7 to 1.0
Molybdenum (Mo), % 3.0 to 3.5
0
Nickel (Ni), % 9.0 to 12
0
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 1.5
0 to 0.4
Sulfur (S), % 0 to 0.030
0 to 0.025