EN 1.4518 Stainless Steel vs. EN 1.8873 Steel

Both EN 1.4518 stainless steel and EN 1.8873 steel are iron alloys. They have 68% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.4518 stainless steel and the bottom bar is EN 1.8873 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 34
19
Fatigue Strength, MPa 160
340
Impact Strength: V-Notched Charpy, J 90
67
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 79
73
Tensile Strength: Ultimate (UTS), MPa 490
660
Tensile Strength: Yield (Proof), MPa 210
490

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1000
420
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 15
39
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
7.8
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
8.9

Otherwise Unclassified Properties

Base Metal Price, % relative 20
3.2
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 4.0
1.8
Embodied Energy, MJ/kg 55
24
Embodied Water, L/kg 160
52

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
110
Resilience: Unit (Modulus of Resilience), kJ/m3 100
650
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 17
23
Strength to Weight: Bending, points 18
21
Thermal Diffusivity, mm2/s 4.1
10
Thermal Shock Resistance, points 14
19

Alloy Composition

Boron (B), % 0
0 to 0.0050
Carbon (C), % 0 to 0.030
0 to 0.18
Chromium (Cr), % 18 to 20
0 to 1.0
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 61.4 to 70
93.6 to 100
Manganese (Mn), % 0 to 1.5
0 to 1.7
Molybdenum (Mo), % 3.0 to 3.5
0 to 0.7
Nickel (Ni), % 9.0 to 12
0 to 1.5
Niobium (Nb), % 0
0 to 0.050
Nitrogen (N), % 0
0 to 0.015
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 1.5
0 to 0.6
Sulfur (S), % 0 to 0.030
0 to 0.010
Titanium (Ti), % 0
0 to 0.050
Vanadium (V), % 0
0 to 0.080
Zirconium (Zr), % 0
0 to 0.15