EN 1.4518 Stainless Steel vs. Solder Alloy 135

EN 1.4518 stainless steel belongs to the iron alloys classification, while solder alloy 135 belongs to the otherwise unclassified metals. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.4518 stainless steel and the bottom bar is solder alloy 135.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
27
Elongation at Break, % 34
20
Poisson's Ratio 0.28
0.41
Shear Modulus, GPa 79
9.5
Tensile Strength: Ultimate (UTS), MPa 490
35

Thermal Properties

Latent Heat of Fusion, J/g 300
36
Melting Completion (Liquidus), °C 1450
250
Melting Onset (Solidus), °C 1400
190
Specific Heat Capacity, J/kg-K 470
160
Thermal Conductivity, W/m-K 15
42
Thermal Expansion, µm/m-K 12
27

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
9.5
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 20
90
Density, g/cm3 7.9
10
Embodied Carbon, kg CO2/kg material 4.0
7.3
Embodied Energy, MJ/kg 55
120
Embodied Water, L/kg 160
720

Common Calculations

Stiffness to Weight: Axial, points 14
1.5
Stiffness to Weight: Bending, points 25
9.9
Strength to Weight: Axial, points 17
1.0
Strength to Weight: Bending, points 18
2.4
Thermal Diffusivity, mm2/s 4.1
27
Thermal Shock Resistance, points 14
3.5

Alloy Composition

Aluminum (Al), % 0
0 to 0.0010
Antimony (Sb), % 0
0.5 to 1.8
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.25
Cadmium (Cd), % 0
0 to 0.0050
Carbon (C), % 0 to 0.030
0
Chromium (Cr), % 18 to 20
0
Copper (Cu), % 0
0 to 0.080
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 61.4 to 70
0 to 0.020
Lead (Pb), % 0
67.1 to 70
Manganese (Mn), % 0 to 1.5
0
Molybdenum (Mo), % 3.0 to 3.5
0
Nickel (Ni), % 9.0 to 12
0 to 0.010
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0 to 1.5
0
Silver (Ag), % 0
0 to 0.1
Sulfur (S), % 0 to 0.030
0
Tin (Sn), % 0
29.5 to 30.5
Zinc (Zn), % 0
0 to 0.0010