EN 1.4518 Stainless Steel vs. Solder Alloy 714

EN 1.4518 stainless steel belongs to the iron alloys classification, while solder alloy 714 belongs to the otherwise unclassified metals. There are 22 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is EN 1.4518 stainless steel and the bottom bar is solder alloy 714.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
51
Elongation at Break, % 34
17
Poisson's Ratio 0.28
0.36
Shear Modulus, GPa 79
19
Tensile Strength: Ultimate (UTS), MPa 490
52

Thermal Properties

Latent Heat of Fusion, J/g 300
62
Melting Completion (Liquidus), °C 1450
220
Melting Onset (Solidus), °C 1400
220
Specific Heat Capacity, J/kg-K 470
220
Thermal Conductivity, W/m-K 15
62
Thermal Expansion, µm/m-K 12
22

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
13
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
16

Otherwise Unclassified Properties

Density, g/cm3 7.9
7.4
Embodied Carbon, kg CO2/kg material 4.0
18
Embodied Energy, MJ/kg 55
300

Common Calculations

Stiffness to Weight: Axial, points 14
3.8
Stiffness to Weight: Bending, points 25
17
Strength to Weight: Axial, points 17
1.9
Strength to Weight: Bending, points 18
4.2
Thermal Diffusivity, mm2/s 4.1
37
Thermal Shock Resistance, points 14
3.3

Alloy Composition

Aluminum (Al), % 0
0 to 0.0010
Antimony (Sb), % 0
0 to 0.1
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.1
Cadmium (Cd), % 0
0 to 0.0020
Carbon (C), % 0 to 0.030
0
Chromium (Cr), % 18 to 20
0
Copper (Cu), % 0
0.3 to 0.7
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 61.4 to 70
0 to 0.020
Lead (Pb), % 0
0 to 0.070
Manganese (Mn), % 0 to 1.5
0
Molybdenum (Mo), % 3.0 to 3.5
0
Nickel (Ni), % 9.0 to 12
0 to 0.010
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0 to 1.5
0
Silver (Ag), % 0
3.8 to 4.2
Sulfur (S), % 0 to 0.030
0
Tin (Sn), % 0
94.6 to 95.9
Zinc (Zn), % 0
0 to 0.0010