EN 1.4518 Stainless Steel vs. N08135 Stainless Steel

Both EN 1.4518 stainless steel and N08135 stainless steel are iron alloys. Both are furnished in the solution annealed (AT) condition. They have 70% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.4518 stainless steel and the bottom bar is N08135 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34
46
Fatigue Strength, MPa 160
220
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 79
80
Tensile Strength: Ultimate (UTS), MPa 490
570
Tensile Strength: Yield (Proof), MPa 210
240

Thermal Properties

Latent Heat of Fusion, J/g 300
310
Maximum Temperature: Corrosion, °C 420
430
Maximum Temperature: Mechanical, °C 1000
1100
Melting Completion (Liquidus), °C 1450
1440
Melting Onset (Solidus), °C 1400
1390
Specific Heat Capacity, J/kg-K 470
460
Thermal Expansion, µm/m-K 12
16

Otherwise Unclassified Properties

Base Metal Price, % relative 20
39
Density, g/cm3 7.9
8.2
Embodied Carbon, kg CO2/kg material 4.0
6.8
Embodied Energy, MJ/kg 55
94
Embodied Water, L/kg 160
220

Common Calculations

PREN (Pitting Resistance) 30
38
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
210
Resilience: Unit (Modulus of Resilience), kJ/m3 100
140
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 17
19
Strength to Weight: Bending, points 18
19
Thermal Shock Resistance, points 14
13

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.030
Chromium (Cr), % 18 to 20
20.5 to 23.5
Copper (Cu), % 0
0 to 0.7
Iron (Fe), % 61.4 to 70
30.2 to 42.3
Manganese (Mn), % 0 to 1.5
0 to 1.0
Molybdenum (Mo), % 3.0 to 3.5
4.0 to 5.0
Nickel (Ni), % 9.0 to 12
33 to 38
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0 to 1.5
0 to 0.75
Sulfur (S), % 0 to 0.030
0 to 0.030
Tungsten (W), % 0
0.2 to 0.8