EN 1.4518 Stainless Steel vs. S20910 Stainless Steel

Both EN 1.4518 stainless steel and S20910 stainless steel are iron alloys. They have a moderately high 90% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.4518 stainless steel and the bottom bar is S20910 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34
14 to 39
Fatigue Strength, MPa 160
310 to 460
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 79
79
Tensile Strength: Ultimate (UTS), MPa 490
780 to 940
Tensile Strength: Yield (Proof), MPa 210
430 to 810

Thermal Properties

Latent Heat of Fusion, J/g 300
300
Maximum Temperature: Corrosion, °C 420
460
Maximum Temperature: Mechanical, °C 1000
1080
Melting Completion (Liquidus), °C 1450
1420
Melting Onset (Solidus), °C 1400
1380
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 15
13
Thermal Expansion, µm/m-K 12
16

Otherwise Unclassified Properties

Base Metal Price, % relative 20
22
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 4.0
4.8
Embodied Energy, MJ/kg 55
68
Embodied Water, L/kg 160
180

Common Calculations

PREN (Pitting Resistance) 30
34
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
120 to 260
Resilience: Unit (Modulus of Resilience), kJ/m3 100
460 to 1640
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 17
28 to 33
Strength to Weight: Bending, points 18
24 to 27
Thermal Diffusivity, mm2/s 4.1
3.6
Thermal Shock Resistance, points 14
17 to 21

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.060
Chromium (Cr), % 18 to 20
20.5 to 23.5
Iron (Fe), % 61.4 to 70
52.1 to 62.1
Manganese (Mn), % 0 to 1.5
4.0 to 6.0
Molybdenum (Mo), % 3.0 to 3.5
1.5 to 3.0
Nickel (Ni), % 9.0 to 12
11.5 to 13.5
Niobium (Nb), % 0
0.1 to 0.3
Nitrogen (N), % 0
0.2 to 0.4
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.5
0 to 0.75
Sulfur (S), % 0 to 0.030
0 to 0.030
Vanadium (V), % 0
0.1 to 0.3