EN 1.4518 Stainless Steel vs. S21640 Stainless Steel

Both EN 1.4518 stainless steel and S21640 stainless steel are iron alloys. They have a moderately high 92% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4518 stainless steel and the bottom bar is S21640 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34
46
Fatigue Strength, MPa 160
320
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 79
78
Tensile Strength: Ultimate (UTS), MPa 490
740
Tensile Strength: Yield (Proof), MPa 210
350

Thermal Properties

Latent Heat of Fusion, J/g 300
290
Maximum Temperature: Corrosion, °C 420
490
Maximum Temperature: Mechanical, °C 1000
940
Melting Completion (Liquidus), °C 1450
1430
Melting Onset (Solidus), °C 1400
1380
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 15
15
Thermal Expansion, µm/m-K 12
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.8

Otherwise Unclassified Properties

Base Metal Price, % relative 20
17
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 4.0
3.6
Embodied Energy, MJ/kg 55
51
Embodied Water, L/kg 160
150

Common Calculations

PREN (Pitting Resistance) 30
26
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
280
Resilience: Unit (Modulus of Resilience), kJ/m3 100
300
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 17
27
Strength to Weight: Bending, points 18
23
Thermal Diffusivity, mm2/s 4.1
4.0
Thermal Shock Resistance, points 14
16

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.080
Chromium (Cr), % 18 to 20
17.5 to 19.5
Iron (Fe), % 61.4 to 70
63 to 74.3
Manganese (Mn), % 0 to 1.5
3.5 to 6.5
Molybdenum (Mo), % 3.0 to 3.5
0.5 to 2.0
Nickel (Ni), % 9.0 to 12
4.0 to 6.5
Niobium (Nb), % 0
0.1 to 1.0
Nitrogen (N), % 0
0.080 to 0.3
Phosphorus (P), % 0 to 0.040
0 to 0.060
Silicon (Si), % 0 to 1.5
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030