EN 1.4530 Stainless Steel vs. K93600 Alloy
Both EN 1.4530 stainless steel and K93600 alloy are iron alloys. There are 12 material properties with values for both materials. Properties with values for just one material (20, in this case) are not shown.
For each property being compared, the top bar is EN 1.4530 stainless steel and the bottom bar is K93600 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 140 |
| Tensile Strength: Ultimate (UTS), MPa | 1030 to 1370 | |
| 480 to 810 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 790 | |
| 440 |
| Melting Onset (Solidus), °C | 1410 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 520 |
| Thermal Expansion, µm/m-K | 11 | |
| 7.3 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.9 | |
| 8.1 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 9.4 |
| Stiffness to Weight: Bending, points | 25 | |
| 21 |
| Strength to Weight: Axial, points | 36 to 48 | |
| 16 to 28 |
| Strength to Weight: Bending, points | 29 to 35 | |
| 17 to 24 |
| Thermal Shock Resistance, points | 35 to 47 | |
| 34 to 57 |