EN 1.4537 Stainless Steel vs. ASTM Grade LC1 Steel

Both EN 1.4537 stainless steel and ASTM grade LC1 steel are iron alloys. They have 43% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.4537 stainless steel and the bottom bar is ASTM grade LC1 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 220
160
Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 42
27
Fatigue Strength, MPa 290
200
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 80
73
Tensile Strength: Ultimate (UTS), MPa 700
540
Tensile Strength: Yield (Proof), MPa 330
270

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1100
410
Melting Completion (Liquidus), °C 1440
1470
Melting Onset (Solidus), °C 1390
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 14
50
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 34
2.4
Density, g/cm3 8.1
7.9
Embodied Carbon, kg CO2/kg material 6.1
1.5
Embodied Energy, MJ/kg 84
20
Embodied Water, L/kg 220
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 240
120
Resilience: Unit (Modulus of Resilience), kJ/m3 270
200
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 24
19
Strength to Weight: Bending, points 22
19
Thermal Diffusivity, mm2/s 3.7
13
Thermal Shock Resistance, points 15
16

Alloy Composition

Carbon (C), % 0 to 0.020
0 to 0.25
Chromium (Cr), % 24 to 26
0
Copper (Cu), % 1.0 to 2.0
0
Iron (Fe), % 36.3 to 46.1
97.6 to 99.05
Manganese (Mn), % 0 to 2.0
0.5 to 0.8
Molybdenum (Mo), % 4.7 to 5.7
0.45 to 0.65
Nickel (Ni), % 24 to 27
0
Nitrogen (N), % 0.17 to 0.25
0
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0 to 0.7
0 to 0.6
Sulfur (S), % 0 to 0.010
0 to 0.045