EN 1.4539 Stainless Steel vs. S35500 Stainless Steel

Both EN 1.4539 stainless steel and S35500 stainless steel are iron alloys. They have 72% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4539 stainless steel and the bottom bar is S35500 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 38
14
Fatigue Strength, MPa 220
690 to 730
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 79
78
Shear Strength, MPa 430
810 to 910
Tensile Strength: Ultimate (UTS), MPa 630
1330 to 1490
Tensile Strength: Yield (Proof), MPa 260
1200 to 1280

Thermal Properties

Latent Heat of Fusion, J/g 300
280
Maximum Temperature: Corrosion, °C 420
440
Maximum Temperature: Mechanical, °C 1100
870
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1390
1420
Specific Heat Capacity, J/kg-K 460
470
Thermal Conductivity, W/m-K 12
16
Thermal Expansion, µm/m-K 16
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 31
16
Density, g/cm3 8.1
7.8
Embodied Carbon, kg CO2/kg material 5.7
3.5
Embodied Energy, MJ/kg 78
47
Embodied Water, L/kg 200
130

Common Calculations

PREN (Pitting Resistance) 36
27
Resilience: Ultimate (Unit Rupture Work), MJ/m3 190
180 to 190
Resilience: Unit (Modulus of Resilience), kJ/m3 160
3610 to 4100
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 22
47 to 53
Strength to Weight: Bending, points 20
34 to 37
Thermal Diffusivity, mm2/s 3.2
4.4
Thermal Shock Resistance, points 14
44 to 49

Alloy Composition

Carbon (C), % 0 to 0.020
0.1 to 0.15
Chromium (Cr), % 19 to 21
15 to 16
Copper (Cu), % 1.2 to 2.0
0
Iron (Fe), % 43.1 to 51.8
73.2 to 77.7
Manganese (Mn), % 0 to 2.0
0.5 to 1.3
Molybdenum (Mo), % 4.0 to 5.0
2.5 to 3.2
Nickel (Ni), % 24 to 26
4.0 to 5.0
Niobium (Nb), % 0
0.1 to 0.5
Nitrogen (N), % 0 to 0.15
0.070 to 0.13
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0 to 0.7
0 to 0.5
Sulfur (S), % 0 to 0.010
0 to 0.030