EN 1.4542 Stainless Steel vs. AISI 420F Stainless Steel
Both EN 1.4542 stainless steel and AISI 420F stainless steel are iron alloys. They have 89% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is EN 1.4542 stainless steel and the bottom bar is AISI 420F stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 5.7 to 20 | |
| 18 |
| Fatigue Strength, MPa | 370 to 640 | |
| 270 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Shear Modulus, GPa | 76 | |
| 76 |
| Shear Strength, MPa | 550 to 860 | |
| 460 |
| Tensile Strength: Ultimate (UTS), MPa | 880 to 1470 | |
| 740 |
| Tensile Strength: Yield (Proof), MPa | 580 to 1300 | |
| 430 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 270 |
| Maximum Temperature: Corrosion, °C | 440 | |
| 390 |
| Maximum Temperature: Mechanical, °C | 860 | |
| 760 |
| Melting Completion (Liquidus), °C | 1430 | |
| 1440 |
| Melting Onset (Solidus), °C | 1380 | |
| 1390 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 480 |
| Thermal Conductivity, W/m-K | 16 | |
| 25 |
| Thermal Expansion, µm/m-K | 11 | |
| 10 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.4 | |
| 3.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.8 | |
| 3.7 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 13 | |
| 7.0 |
| Density, g/cm3 | 7.8 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 2.0 |
| Embodied Energy, MJ/kg | 39 | |
| 28 |
| Embodied Water, L/kg | 130 | |
| 100 |
Common Calculations
| PREN (Pitting Resistance) | 17 | |
| 14 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 62 to 160 | |
| 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 880 to 4360 | |
| 480 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 31 to 52 | |
| 27 |
| Strength to Weight: Bending, points | 26 to 37 | |
| 23 |
| Thermal Diffusivity, mm2/s | 4.3 | |
| 6.8 |
| Thermal Shock Resistance, points | 29 to 49 | |
| 27 |
Alloy Composition
| Carbon (C), % | 0 to 0.070 | |
| 0.3 to 0.4 |
| Chromium (Cr), % | 15 to 17 | |
| 12 to 14 |
| Copper (Cu), % | 3.0 to 5.0 | |
| 0 |
| Iron (Fe), % | 69.6 to 79 | |
| 82.4 to 87.6 |
| Manganese (Mn), % | 0 to 1.5 | |
| 0 to 1.3 |
| Molybdenum (Mo), % | 0 to 0.6 | |
| 0 to 0.5 |
| Nickel (Ni), % | 3.0 to 5.0 | |
| 0 |
| Niobium (Nb), % | 0 to 0.45 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.060 |
| Silicon (Si), % | 0 to 0.7 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.015 | |
| 0.15 to 0.35 |