EN 1.4542 Stainless Steel vs. EN 1.0258 Steel

Both EN 1.4542 stainless steel and EN 1.0258 steel are iron alloys. They have 76% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.4542 stainless steel and the bottom bar is EN 1.0258 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 5.7 to 20
23
Fatigue Strength, MPa 370 to 640
200
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Shear Strength, MPa 550 to 860
310
Tensile Strength: Ultimate (UTS), MPa 880 to 1470
490
Tensile Strength: Yield (Proof), MPa 580 to 1300
290

Thermal Properties

Latent Heat of Fusion, J/g 280
250
Maximum Temperature: Mechanical, °C 860
400
Melting Completion (Liquidus), °C 1430
1460
Melting Onset (Solidus), °C 1380
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 16
49
Thermal Expansion, µm/m-K 11
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.8
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 13
2.1
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 2.7
1.5
Embodied Energy, MJ/kg 39
19
Embodied Water, L/kg 130
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 62 to 160
95
Resilience: Unit (Modulus of Resilience), kJ/m3 880 to 4360
220
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 31 to 52
17
Strength to Weight: Bending, points 26 to 37
18
Thermal Diffusivity, mm2/s 4.3
13
Thermal Shock Resistance, points 29 to 49
16

Alloy Composition

Carbon (C), % 0 to 0.070
0 to 0.2
Chromium (Cr), % 15 to 17
0 to 0.3
Copper (Cu), % 3.0 to 5.0
0 to 0.3
Iron (Fe), % 69.6 to 79
96.9 to 100
Manganese (Mn), % 0 to 1.5
0 to 1.4
Molybdenum (Mo), % 0 to 0.6
0 to 0.080
Nickel (Ni), % 3.0 to 5.0
0 to 0.3
Niobium (Nb), % 0 to 0.45
0 to 0.010
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 0.7
0 to 0.4
Sulfur (S), % 0 to 0.015
0 to 0.020
Titanium (Ti), % 0
0 to 0.040
Vanadium (V), % 0
0 to 0.020