EN 1.4542 Stainless Steel vs. EN 1.4435 Stainless Steel

Both EN 1.4542 stainless steel and EN 1.4435 stainless steel are iron alloys. They have 85% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4542 stainless steel and the bottom bar is EN 1.4435 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 5.7 to 20
43
Fatigue Strength, MPa 370 to 640
220
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
78
Shear Strength, MPa 550 to 860
420
Tensile Strength: Ultimate (UTS), MPa 880 to 1470
610
Tensile Strength: Yield (Proof), MPa 580 to 1300
240

Thermal Properties

Latent Heat of Fusion, J/g 280
290
Maximum Temperature: Corrosion, °C 440
420
Maximum Temperature: Mechanical, °C 860
980
Melting Completion (Liquidus), °C 1430
1440
Melting Onset (Solidus), °C 1380
1400
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 16
15
Thermal Expansion, µm/m-K 11
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.8
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 13
21
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 2.7
4.1
Embodied Energy, MJ/kg 39
57
Embodied Water, L/kg 130
160

Common Calculations

PREN (Pitting Resistance) 17
28
Resilience: Ultimate (Unit Rupture Work), MJ/m3 62 to 160
210
Resilience: Unit (Modulus of Resilience), kJ/m3 880 to 4360
150
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 31 to 52
21
Strength to Weight: Bending, points 26 to 37
20
Thermal Diffusivity, mm2/s 4.3
4.0
Thermal Shock Resistance, points 29 to 49
14

Alloy Composition

Carbon (C), % 0 to 0.070
0 to 0.030
Chromium (Cr), % 15 to 17
17 to 19
Copper (Cu), % 3.0 to 5.0
0
Iron (Fe), % 69.6 to 79
59.8 to 68
Manganese (Mn), % 0 to 1.5
0 to 2.0
Molybdenum (Mo), % 0 to 0.6
2.5 to 3.0
Nickel (Ni), % 3.0 to 5.0
12.5 to 15
Niobium (Nb), % 0 to 0.45
0
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 0 to 0.7
0 to 1.0
Sulfur (S), % 0 to 0.015
0 to 0.015