EN 1.4542 Stainless Steel vs. EN 1.5514 Steel

Both EN 1.4542 stainless steel and EN 1.5514 steel are iron alloys. They have 76% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is EN 1.4542 stainless steel and the bottom bar is EN 1.5514 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Tensile Strength: Ultimate (UTS), MPa 880 to 1470
470 to 1680

Thermal Properties

Latent Heat of Fusion, J/g 280
250
Maximum Temperature: Mechanical, °C 860
400
Melting Completion (Liquidus), °C 1430
1460
Melting Onset (Solidus), °C 1380
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 16
49
Thermal Expansion, µm/m-K 11
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.8
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 13
1.9
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 2.7
1.4
Embodied Energy, MJ/kg 39
19
Embodied Water, L/kg 130
47

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 31 to 52
17 to 60
Strength to Weight: Bending, points 26 to 37
17 to 40
Thermal Diffusivity, mm2/s 4.3
13
Thermal Shock Resistance, points 29 to 49
14 to 50

Alloy Composition

Boron (B), % 0
0.00080 to 0.0050
Carbon (C), % 0 to 0.070
0.3 to 0.35
Chromium (Cr), % 15 to 17
0 to 0.3
Copper (Cu), % 3.0 to 5.0
0 to 0.25
Iron (Fe), % 69.6 to 79
97.8 to 99.099
Manganese (Mn), % 0 to 1.5
0.6 to 0.9
Molybdenum (Mo), % 0 to 0.6
0
Nickel (Ni), % 3.0 to 5.0
0
Niobium (Nb), % 0 to 0.45
0
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 0.7
0 to 0.3
Sulfur (S), % 0 to 0.015
0 to 0.025