EN 1.4578 Stainless Steel vs. ASTM Grade LC1 Steel

Both EN 1.4578 stainless steel and ASTM grade LC1 steel are iron alloys. They have 67% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.4578 stainless steel and the bottom bar is ASTM grade LC1 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
160
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 51
27
Fatigue Strength, MPa 200
200
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Tensile Strength: Ultimate (UTS), MPa 550
540
Tensile Strength: Yield (Proof), MPa 200
270

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 930
410
Melting Completion (Liquidus), °C 1430
1470
Melting Onset (Solidus), °C 1390
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 14
50
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.3
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.6
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 19
2.4
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 3.7
1.5
Embodied Energy, MJ/kg 51
20
Embodied Water, L/kg 160
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 220
120
Resilience: Unit (Modulus of Resilience), kJ/m3 100
200
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 19
19
Strength to Weight: Bending, points 19
19
Thermal Diffusivity, mm2/s 3.9
13
Thermal Shock Resistance, points 12
16

Alloy Composition

Carbon (C), % 0 to 0.040
0 to 0.25
Chromium (Cr), % 16.5 to 17.5
0
Copper (Cu), % 3.0 to 3.5
0
Iron (Fe), % 62.3 to 68.5
97.6 to 99.05
Manganese (Mn), % 0 to 2.0
0.5 to 0.8
Molybdenum (Mo), % 2.0 to 2.5
0.45 to 0.65
Nickel (Ni), % 10 to 11
0
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 0.6
Sulfur (S), % 0 to 0.015
0 to 0.045