EN 1.4581 Stainless Steel vs. SAE-AISI 1065 Steel

Both EN 1.4581 stainless steel and SAE-AISI 1065 steel are iron alloys. They have 67% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.4581 stainless steel and the bottom bar is SAE-AISI 1065 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
210 to 230
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 28
11 to 14
Fatigue Strength, MPa 150
270 to 340
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
72
Tensile Strength: Ultimate (UTS), MPa 510
710 to 780
Tensile Strength: Yield (Proof), MPa 210
430 to 550

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 990
400
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 15
51
Thermal Expansion, µm/m-K 16
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
11
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
12

Otherwise Unclassified Properties

Base Metal Price, % relative 21
1.8
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 4.2
1.4
Embodied Energy, MJ/kg 59
19
Embodied Water, L/kg 160
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
74 to 90
Resilience: Unit (Modulus of Resilience), kJ/m3 110
490 to 820
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 18
25 to 28
Strength to Weight: Bending, points 18
23 to 24
Thermal Diffusivity, mm2/s 3.9
14
Thermal Shock Resistance, points 12
25 to 27

Alloy Composition

Carbon (C), % 0 to 0.070
0.6 to 0.7
Chromium (Cr), % 18 to 20
0
Iron (Fe), % 61.4 to 71
98.3 to 98.8
Manganese (Mn), % 0 to 1.5
0.6 to 0.9
Molybdenum (Mo), % 2.0 to 2.5
0
Nickel (Ni), % 9.0 to 12
0
Niobium (Nb), % 0 to 1.0
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.5
0
Sulfur (S), % 0 to 0.030
0 to 0.050