EN 1.4587 Stainless Steel vs. EN 1.0116 Steel

Both EN 1.4587 stainless steel and EN 1.0116 steel are iron alloys. They have a modest 39% of their average alloy composition in common, which, by itself, doesn't mean much. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4587 stainless steel and the bottom bar is EN 1.0116 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160
110
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 34
23
Fatigue Strength, MPa 200
140
Impact Strength: V-Notched Charpy, J 67
28
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 80
73
Tensile Strength: Ultimate (UTS), MPa 540
380
Tensile Strength: Yield (Proof), MPa 250
200

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1420
1460
Melting Onset (Solidus), °C 1370
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 17
49
Thermal Expansion, µm/m-K 15
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.8
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.0
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 36
2.0
Density, g/cm3 8.1
7.8
Embodied Carbon, kg CO2/kg material 6.3
1.4
Embodied Energy, MJ/kg 87
19
Embodied Water, L/kg 230
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 150
72
Resilience: Unit (Modulus of Resilience), kJ/m3 150
110
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 18
13
Strength to Weight: Bending, points 18
15
Thermal Diffusivity, mm2/s 4.5
13
Thermal Shock Resistance, points 13
12

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.17
Chromium (Cr), % 24 to 26
0 to 0.3
Copper (Cu), % 2.0 to 3.0
0
Iron (Fe), % 32.7 to 41.9
97.1 to 100
Manganese (Mn), % 0 to 2.0
0 to 1.4
Molybdenum (Mo), % 4.0 to 5.0
0 to 0.080
Nickel (Ni), % 28 to 30
0 to 0.3
Nitrogen (N), % 0.15 to 0.25
0
Phosphorus (P), % 0 to 0.035
0 to 0.035
Silicon (Si), % 0 to 1.0
0 to 0.55
Sulfur (S), % 0 to 0.025
0 to 0.035