EN 1.4587 Stainless Steel vs. EN 1.8868 Steel

Both EN 1.4587 stainless steel and EN 1.8868 steel are iron alloys. They have a modest 39% of their average alloy composition in common, which, by itself, doesn't mean much. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4587 stainless steel and the bottom bar is EN 1.8868 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160
160
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 34
25
Fatigue Strength, MPa 200
260
Impact Strength: V-Notched Charpy, J 67
90
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 80
73
Tensile Strength: Ultimate (UTS), MPa 540
540
Tensile Strength: Yield (Proof), MPa 250
350

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1100
410
Melting Completion (Liquidus), °C 1420
1460
Melting Onset (Solidus), °C 1370
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 17
48
Thermal Expansion, µm/m-K 15
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.8
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.0
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 36
2.4
Density, g/cm3 8.1
7.9
Embodied Carbon, kg CO2/kg material 6.3
1.6
Embodied Energy, MJ/kg 87
21
Embodied Water, L/kg 230
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 150
120
Resilience: Unit (Modulus of Resilience), kJ/m3 150
330
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 18
19
Strength to Weight: Bending, points 18
19
Thermal Diffusivity, mm2/s 4.5
13
Thermal Shock Resistance, points 13
16

Alloy Composition

Boron (B), % 0
0 to 0.0050
Carbon (C), % 0 to 0.030
0 to 0.16
Chromium (Cr), % 24 to 26
0 to 0.3
Copper (Cu), % 2.0 to 3.0
0 to 0.3
Iron (Fe), % 32.7 to 41.9
96.4 to 100
Manganese (Mn), % 0 to 2.0
0 to 1.5
Molybdenum (Mo), % 4.0 to 5.0
0 to 0.25
Nickel (Ni), % 28 to 30
0 to 0.5
Niobium (Nb), % 0
0 to 0.050
Nitrogen (N), % 0.15 to 0.25
0 to 0.015
Phosphorus (P), % 0 to 0.035
0 to 0.020
Silicon (Si), % 0 to 1.0
0 to 0.4
Sulfur (S), % 0 to 0.025
0 to 0.0080
Titanium (Ti), % 0
0 to 0.030
Vanadium (V), % 0
0 to 0.060
Zirconium (Zr), % 0
0 to 0.050