EN 1.4587 Stainless Steel vs. SAE-AISI D2 Steel

Both EN 1.4587 stainless steel and SAE-AISI D2 steel are iron alloys. They have 51% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.4587 stainless steel and the bottom bar is SAE-AISI D2 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 34
5.0 to 16
Fatigue Strength, MPa 200
310 to 860
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 80
75
Tensile Strength: Ultimate (UTS), MPa 540
760 to 2000
Tensile Strength: Yield (Proof), MPa 250
470 to 1510

Thermal Properties

Latent Heat of Fusion, J/g 310
270
Melting Completion (Liquidus), °C 1420
1440
Melting Onset (Solidus), °C 1370
1390
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 17
31
Thermal Expansion, µm/m-K 15
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.8
4.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.0
5.1

Otherwise Unclassified Properties

Base Metal Price, % relative 36
8.0
Density, g/cm3 8.1
7.7
Embodied Carbon, kg CO2/kg material 6.3
3.4
Embodied Energy, MJ/kg 87
50
Embodied Water, L/kg 230
100

Common Calculations

PREN (Pitting Resistance) 43
15
Resilience: Ultimate (Unit Rupture Work), MJ/m3 150
92 to 100
Resilience: Unit (Modulus of Resilience), kJ/m3 150
570 to 5940
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 18
27 to 72
Strength to Weight: Bending, points 18
24 to 46
Thermal Diffusivity, mm2/s 4.5
8.3
Thermal Shock Resistance, points 13
25 to 67

Alloy Composition

Carbon (C), % 0 to 0.030
1.4 to 1.6
Chromium (Cr), % 24 to 26
11 to 13
Copper (Cu), % 2.0 to 3.0
0 to 0.25
Iron (Fe), % 32.7 to 41.9
81.3 to 86.9
Manganese (Mn), % 0 to 2.0
0 to 0.6
Molybdenum (Mo), % 4.0 to 5.0
0.7 to 1.2
Nickel (Ni), % 28 to 30
0 to 0.3
Nitrogen (N), % 0.15 to 0.25
0
Phosphorus (P), % 0 to 0.035
0 to 0.030
Silicon (Si), % 0 to 1.0
0 to 0.6
Sulfur (S), % 0 to 0.025
0 to 0.030
Vanadium (V), % 0
0 to 1.1