EN 1.4606 Stainless Steel vs. ASTM A283 Carbon Steel
Both EN 1.4606 stainless steel and ASTM A283 carbon steel are iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is EN 1.4606 stainless steel and the bottom bar is ASTM A283 carbon steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 23 to 39 | |
| 26 to 34 |
| Fatigue Strength, MPa | 240 to 420 | |
| 150 to 190 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 75 | |
| 73 |
| Shear Strength, MPa | 410 to 640 | |
| 240 to 310 |
| Tensile Strength: Ultimate (UTS), MPa | 600 to 1020 | |
| 360 to 480 |
| Tensile Strength: Yield (Proof), MPa | 280 to 630 | |
| 180 to 260 |
Thermal Properties
| Latent Heat of Fusion, J/g | 300 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 910 | |
| 400 |
| Melting Completion (Liquidus), °C | 1430 | |
| 1460 |
| Melting Onset (Solidus), °C | 1380 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 14 | |
| 51 to 53 |
| Thermal Expansion, µm/m-K | 11 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.9 | |
| 7.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.2 | |
| 8.1 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 26 | |
| 1.8 |
| Density, g/cm3 | 7.9 | |
| 7.8 to 7.9 |
| Embodied Carbon, kg CO2/kg material | 6.0 | |
| 1.4 |
| Embodied Energy, MJ/kg | 87 | |
| 18 |
| Embodied Water, L/kg | 170 | |
| 46 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 190 to 200 | |
| 100 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 200 to 1010 | |
| 91 to 180 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 21 to 36 | |
| 13 to 17 |
| Strength to Weight: Bending, points | 20 to 28 | |
| 14 to 17 |
| Thermal Diffusivity, mm2/s | 3.7 | |
| 14 |
| Thermal Shock Resistance, points | 21 to 35 | |
| 11 to 15 |