EN 1.4806 Stainless Steel vs. EN 1.4578 Stainless Steel

Both EN 1.4806 stainless steel and EN 1.4578 stainless steel are iron alloys. They have 74% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4806 stainless steel and the bottom bar is EN 1.4578 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
190
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 6.8
51
Fatigue Strength, MPa 120
200
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 75
77
Tensile Strength: Ultimate (UTS), MPa 470
550
Tensile Strength: Yield (Proof), MPa 250
200

Thermal Properties

Latent Heat of Fusion, J/g 320
290
Maximum Temperature: Corrosion, °C 400
410
Maximum Temperature: Mechanical, °C 1000
930
Melting Completion (Liquidus), °C 1380
1430
Melting Onset (Solidus), °C 1340
1390
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 12
14
Thermal Expansion, µm/m-K 15
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 31
19
Density, g/cm3 8.0
7.9
Embodied Carbon, kg CO2/kg material 5.4
3.7
Embodied Energy, MJ/kg 76
51
Embodied Water, L/kg 190
160

Common Calculations

PREN (Pitting Resistance) 18
25
Resilience: Ultimate (Unit Rupture Work), MJ/m3 27
220
Resilience: Unit (Modulus of Resilience), kJ/m3 160
100
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 16
19
Strength to Weight: Bending, points 17
19
Thermal Diffusivity, mm2/s 3.1
3.9
Thermal Shock Resistance, points 11
12

Alloy Composition

Carbon (C), % 0.3 to 0.5
0 to 0.040
Chromium (Cr), % 16 to 18
16.5 to 17.5
Copper (Cu), % 0
3.0 to 3.5
Iron (Fe), % 40.4 to 48.7
62.3 to 68.5
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 0 to 0.5
2.0 to 2.5
Nickel (Ni), % 34 to 36
10 to 11
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 1.0 to 2.5
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.015