EN 1.4806 Stainless Steel vs. EN 1.4935 Stainless Steel

Both EN 1.4806 stainless steel and EN 1.4935 stainless steel are iron alloys. They have 58% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4806 stainless steel and the bottom bar is EN 1.4935 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 6.8
16 to 18
Fatigue Strength, MPa 120
350 to 400
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 75
76
Tensile Strength: Ultimate (UTS), MPa 470
780 to 880
Tensile Strength: Yield (Proof), MPa 250
570 to 670

Thermal Properties

Latent Heat of Fusion, J/g 320
270
Maximum Temperature: Corrosion, °C 400
380
Maximum Temperature: Mechanical, °C 1000
740
Melting Completion (Liquidus), °C 1380
1460
Melting Onset (Solidus), °C 1340
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 12
24
Thermal Expansion, µm/m-K 15
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 31
9.0
Density, g/cm3 8.0
7.8
Embodied Carbon, kg CO2/kg material 5.4
2.9
Embodied Energy, MJ/kg 76
42
Embodied Water, L/kg 190
100

Common Calculations

PREN (Pitting Resistance) 18
16
Resilience: Ultimate (Unit Rupture Work), MJ/m3 27
130
Resilience: Unit (Modulus of Resilience), kJ/m3 160
830 to 1160
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 16
28 to 31
Strength to Weight: Bending, points 17
24 to 26
Thermal Diffusivity, mm2/s 3.1
6.5
Thermal Shock Resistance, points 11
27 to 30

Alloy Composition

Carbon (C), % 0.3 to 0.5
0.17 to 0.24
Chromium (Cr), % 16 to 18
11 to 12.5
Iron (Fe), % 40.4 to 48.7
83 to 86.7
Manganese (Mn), % 0 to 2.0
0.3 to 0.8
Molybdenum (Mo), % 0 to 0.5
0.8 to 1.2
Nickel (Ni), % 34 to 36
0.3 to 0.8
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 1.0 to 2.5
0.1 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.015
Tungsten (W), % 0
0.4 to 0.6
Vanadium (V), % 0
0.2 to 0.35