EN 1.4806 Stainless Steel vs. EN 1.4959 Stainless Steel

Both EN 1.4806 stainless steel and EN 1.4959 stainless steel are iron alloys. They have a moderately high 95% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4806 stainless steel and the bottom bar is EN 1.4959 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 6.8
40
Fatigue Strength, MPa 120
170
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 75
77
Tensile Strength: Ultimate (UTS), MPa 470
630
Tensile Strength: Yield (Proof), MPa 250
190

Thermal Properties

Latent Heat of Fusion, J/g 320
300
Maximum Temperature: Corrosion, °C 400
510
Maximum Temperature: Mechanical, °C 1000
1090
Melting Completion (Liquidus), °C 1380
1400
Melting Onset (Solidus), °C 1340
1350
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 12
12
Thermal Expansion, µm/m-K 15
15

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
2.0

Otherwise Unclassified Properties

Base Metal Price, % relative 31
31
Density, g/cm3 8.0
8.0
Embodied Carbon, kg CO2/kg material 5.4
5.4
Embodied Energy, MJ/kg 76
76
Embodied Water, L/kg 190
200

Common Calculations

PREN (Pitting Resistance) 18
21
Resilience: Ultimate (Unit Rupture Work), MJ/m3 27
190
Resilience: Unit (Modulus of Resilience), kJ/m3 160
96
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 16
22
Strength to Weight: Bending, points 17
20
Thermal Diffusivity, mm2/s 3.1
3.2
Thermal Shock Resistance, points 11
15

Alloy Composition

Aluminum (Al), % 0
0.25 to 0.65
Carbon (C), % 0.3 to 0.5
0.050 to 0.1
Chromium (Cr), % 16 to 18
19 to 22
Cobalt (Co), % 0
0 to 0.5
Copper (Cu), % 0
0 to 0.5
Iron (Fe), % 40.4 to 48.7
39.4 to 50.5
Manganese (Mn), % 0 to 2.0
0 to 1.5
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 34 to 36
30 to 34
Nitrogen (N), % 0
0 to 0.030
Phosphorus (P), % 0 to 0.040
0 to 0.015
Silicon (Si), % 1.0 to 2.5
0 to 0.7
Sulfur (S), % 0 to 0.030
0 to 0.010
Titanium (Ti), % 0
0.25 to 0.65