EN 1.4806 Stainless Steel vs. S44537 Stainless Steel

Both EN 1.4806 stainless steel and S44537 stainless steel are iron alloys. They have 63% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4806 stainless steel and the bottom bar is S44537 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
180
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 6.8
21
Fatigue Strength, MPa 120
230
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 75
79
Tensile Strength: Ultimate (UTS), MPa 470
510
Tensile Strength: Yield (Proof), MPa 250
360

Thermal Properties

Latent Heat of Fusion, J/g 320
290
Maximum Temperature: Corrosion, °C 400
530
Maximum Temperature: Mechanical, °C 1000
1000
Melting Completion (Liquidus), °C 1380
1480
Melting Onset (Solidus), °C 1340
1430
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 12
21
Thermal Expansion, µm/m-K 15
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
2.6
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
3.0

Otherwise Unclassified Properties

Base Metal Price, % relative 31
19
Density, g/cm3 8.0
7.9
Embodied Carbon, kg CO2/kg material 5.4
3.4
Embodied Energy, MJ/kg 76
50
Embodied Water, L/kg 190
140

Common Calculations

PREN (Pitting Resistance) 18
26
Resilience: Ultimate (Unit Rupture Work), MJ/m3 27
95
Resilience: Unit (Modulus of Resilience), kJ/m3 160
320
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 16
18
Strength to Weight: Bending, points 17
18
Thermal Diffusivity, mm2/s 3.1
5.6
Thermal Shock Resistance, points 11
17

Alloy Composition

Aluminum (Al), % 0
0 to 0.1
Carbon (C), % 0.3 to 0.5
0 to 0.030
Chromium (Cr), % 16 to 18
20 to 24
Copper (Cu), % 0
0 to 0.5
Iron (Fe), % 40.4 to 48.7
69 to 78.6
Lanthanum (La), % 0
0.040 to 0.2
Manganese (Mn), % 0 to 2.0
0 to 0.8
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 34 to 36
0 to 0.5
Niobium (Nb), % 0
0.2 to 1.0
Nitrogen (N), % 0
0 to 0.040
Phosphorus (P), % 0 to 0.040
0 to 0.050
Silicon (Si), % 1.0 to 2.5
0.1 to 0.6
Sulfur (S), % 0 to 0.030
0 to 0.0060
Titanium (Ti), % 0
0.020 to 0.2
Tungsten (W), % 0
1.0 to 3.0