MakeItFrom.com
Menu (ESC)

EN 1.4807 Stainless Steel vs. AWS E312

Both EN 1.4807 stainless steel and AWS E312 are iron alloys. They have 71% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is EN 1.4807 stainless steel and the bottom bar is AWS E312.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 4.5
25
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 75
80
Tensile Strength: Ultimate (UTS), MPa 480
740

Thermal Properties

Latent Heat of Fusion, J/g 320
310
Melting Completion (Liquidus), °C 1390
1410
Melting Onset (Solidus), °C 1350
1360
Specific Heat Capacity, J/kg-K 480
480
Thermal Expansion, µm/m-K 15
15

Otherwise Unclassified Properties

Base Metal Price, % relative 39
20
Density, g/cm3 8.0
7.7
Embodied Carbon, kg CO2/kg material 6.8
3.6
Embodied Energy, MJ/kg 97
52
Embodied Water, L/kg 190
200

Common Calculations

PREN (Pitting Resistance) 19
31
Stiffness to Weight: Axial, points 13
15
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 17
27
Strength to Weight: Bending, points 17
24
Thermal Shock Resistance, points 12
18

Alloy Composition

Carbon (C), % 0.3 to 0.5
0 to 0.15
Chromium (Cr), % 17 to 20
28 to 32
Copper (Cu), % 0
0 to 0.75
Iron (Fe), % 36.6 to 46.7
52.3 to 63.5
Manganese (Mn), % 0 to 2.0
0.5 to 2.5
Molybdenum (Mo), % 0 to 0.5
0 to 0.75
Nickel (Ni), % 34 to 36
8.0 to 10.5
Niobium (Nb), % 1.0 to 1.8
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 1.0 to 2.5
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030