EN 1.4826 Stainless Steel vs. EN 1.4123 Stainless Steel

Both EN 1.4826 stainless steel and EN 1.4123 stainless steel are iron alloys. They have 82% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.4826 stainless steel and the bottom bar is EN 1.4123 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
220 to 250
Elastic (Young's, Tensile) Modulus, GPa 200
200
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
77
Tensile Strength: Ultimate (UTS), MPa 500
720 to 810

Thermal Properties

Latent Heat of Fusion, J/g 310
280
Maximum Temperature: Corrosion, °C 430
390
Maximum Temperature: Mechanical, °C 950
840
Melting Completion (Liquidus), °C 1400
1450
Melting Onset (Solidus), °C 1360
1410
Specific Heat Capacity, J/kg-K 490
480
Thermal Conductivity, W/m-K 14
23
Thermal Expansion, µm/m-K 16
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.8

Otherwise Unclassified Properties

Base Metal Price, % relative 17
10
Density, g/cm3 7.7
7.7
Embodied Carbon, kg CO2/kg material 3.3
4.2
Embodied Energy, MJ/kg 47
62
Embodied Water, L/kg 160
120

Common Calculations

PREN (Pitting Resistance) 23
24
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 18
26 to 29
Strength to Weight: Bending, points 18
23 to 25
Thermal Diffusivity, mm2/s 3.7
6.3
Thermal Shock Resistance, points 11
26 to 29

Alloy Composition

Carbon (C), % 0.3 to 0.5
0.35 to 0.5
Chromium (Cr), % 21 to 23
14 to 16.5
Iron (Fe), % 60.4 to 68.7
76.7 to 84.6
Manganese (Mn), % 0 to 2.0
0 to 1.0
Molybdenum (Mo), % 0 to 0.5
1.0 to 2.5
Nickel (Ni), % 9.0 to 11
0 to 0.5
Nitrogen (N), % 0
0.1 to 0.3
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 1.0 to 2.5
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030
Vanadium (V), % 0
0 to 1.5