EN 1.4826 Stainless Steel vs. EN 1.5662 Steel

Both EN 1.4826 stainless steel and EN 1.5662 steel are iron alloys. They have 75% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is EN 1.4826 stainless steel and the bottom bar is EN 1.5662 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
220 to 230
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 9.1
20
Fatigue Strength, MPa 140
380 to 450
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Tensile Strength: Ultimate (UTS), MPa 500
740 to 750
Tensile Strength: Yield (Proof), MPa 260
550 to 660

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 950
430
Melting Completion (Liquidus), °C 1400
1460
Melting Onset (Solidus), °C 1360
1410
Specific Heat Capacity, J/kg-K 490
470
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
8.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
9.8

Otherwise Unclassified Properties

Base Metal Price, % relative 17
7.5
Density, g/cm3 7.7
8.0
Embodied Carbon, kg CO2/kg material 3.3
2.3
Embodied Energy, MJ/kg 47
31
Embodied Water, L/kg 160
63

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 39
140 to 150
Resilience: Unit (Modulus of Resilience), kJ/m3 170
810 to 1150
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 18
26
Strength to Weight: Bending, points 18
23
Thermal Shock Resistance, points 11
22

Alloy Composition

Carbon (C), % 0.3 to 0.5
0 to 0.1
Chromium (Cr), % 21 to 23
0
Iron (Fe), % 60.4 to 68.7
88.6 to 91.2
Manganese (Mn), % 0 to 2.0
0.3 to 0.8
Molybdenum (Mo), % 0 to 0.5
0 to 0.1
Nickel (Ni), % 9.0 to 11
8.5 to 10
Phosphorus (P), % 0 to 0.040
0 to 0.020
Silicon (Si), % 1.0 to 2.5
0 to 0.35
Sulfur (S), % 0 to 0.030
0 to 0.0050
Vanadium (V), % 0
0 to 0.050