EN 1.4832 Stainless Steel vs. EN 1.6217 Steel

Both EN 1.4832 stainless steel and EN 1.6217 steel are iron alloys. They have 65% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.4832 stainless steel and the bottom bar is EN 1.6217 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
170
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 11
24
Fatigue Strength, MPa 140
280
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Tensile Strength: Ultimate (UTS), MPa 510
550
Tensile Strength: Yield (Proof), MPa 260
390

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 950
400
Melting Completion (Liquidus), °C 1400
1460
Melting Onset (Solidus), °C 1360
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 14
50
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 19
2.3
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.6
1.5
Embodied Energy, MJ/kg 51
21
Embodied Water, L/kg 160
49

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 48
120
Resilience: Unit (Modulus of Resilience), kJ/m3 170
410
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 18
19
Strength to Weight: Bending, points 18
19
Thermal Diffusivity, mm2/s 3.7
14
Thermal Shock Resistance, points 12
16

Alloy Composition

Aluminum (Al), % 0
0.020 to 0.050
Carbon (C), % 0.15 to 0.35
0 to 0.16
Chromium (Cr), % 19 to 21
0
Iron (Fe), % 58.6 to 67.4
96.6 to 99
Manganese (Mn), % 0 to 2.0
0.85 to 1.7
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 13 to 15
0.15 to 0.85
Niobium (Nb), % 0
0 to 0.050
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0.5 to 2.5
0 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.010
Vanadium (V), % 0
0 to 0.050