EN 1.4864 Stainless Steel vs. AWS E330

Both EN 1.4864 stainless steel and AWS E330 are iron alloys. They have a very high 98% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.4864 stainless steel and the bottom bar is AWS E330.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 33
29
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 75
76
Tensile Strength: Ultimate (UTS), MPa 650
580

Thermal Properties

Latent Heat of Fusion, J/g 310
300
Melting Completion (Liquidus), °C 1390
1400
Melting Onset (Solidus), °C 1340
1350
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 13
12
Thermal Expansion, µm/m-K 14
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 30
31
Density, g/cm3 8.0
8.1
Embodied Carbon, kg CO2/kg material 5.3
5.4
Embodied Energy, MJ/kg 75
75
Embodied Water, L/kg 180
180

Common Calculations

PREN (Pitting Resistance) 17
17
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 23
20
Strength to Weight: Bending, points 21
19
Thermal Diffusivity, mm2/s 3.3
3.2
Thermal Shock Resistance, points 17
16

Alloy Composition

Carbon (C), % 0 to 0.15
0.18 to 0.25
Chromium (Cr), % 15 to 17
14 to 17
Copper (Cu), % 0
0 to 0.75
Iron (Fe), % 41.7 to 51
40.7 to 51.8
Manganese (Mn), % 0 to 2.0
1.0 to 2.5
Molybdenum (Mo), % 0
0 to 0.75
Nickel (Ni), % 33 to 37
33 to 37
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 1.0 to 2.0
0 to 1.0
Sulfur (S), % 0 to 0.015
0 to 0.030